Galactic Oil Spot Glazes

An interesting view of my most recent round of test glazes. Each Oil Spot variation was dipped in porcelain and red stoneware  with the red stoneware tiles shown. The firing was: 10 hr oxidation to Cone 7, 2hr oxidation slow climb to Cone 8, 3 hr slow climb to cone 10, 1 hour oxidation hold @ cone 10. The results were pretty cool, and under magnification they had just the right amount of galactic goodness. The pictures were taken with a USB digital microscope! Magnification is about 30-40x

For the longest time I’ve wanted to try firing oil spot glazes, and after a bit of research it was pretty satisfying to make it happen. I decided to begin by concentrating on black, single glaze variations – the recipes of which came from a number of sources, mainly John Britt’s ebook and Complete Guide to High Fire glazes, a few from Michael Bailey’s Oriental Glazes, and a couple from Hopper’s The Ceramic Spectrum. The next step is to start zeroing in on some of the more spectacular variations and then start changing up the recipes and the firing schedules for maximum effect. Enjoy!

What I’ve been up to…

Ice crackle using some of the last of my old stoneware recipe leftover from my move from the Armory.
Ice crackle using some of the last of my old stoneware recipe leftover from my move from the Armory. Not amazing, but not nearly as much trouble getting these glazes to work. The lack of iron in the clay body is what’s keeping the rim from being what I like the most.
More materials.
Local materials. Sandstone, metamorphosed sandstone, quartzite (possible limestone schist), black dolomite, marble, limestone
Materials prospected extremely close to the studio
Materials prospected extremely close to the studio, more prospected glaze material tests. Soda rich mud stone on the back right – it’s gonna make a wicked carbon trap shino.
The  new workspace.
The new workspace. Complete with Insight glaze chem software, which I know understand.,
The clay body tests in Bisque, c6, c10, c10redux, soda, redux cool
The clay body tests in Bisque, c6, c10, c10redux, soda, redux cool. Lots of work, this. What’s not pictured is the hour and hour and hours of firing brand new kilns.
Locally prospected tests.
Locally prospected tests. For those folks still in West Palm, Aplite is the railroad track gravel east of the studio. AWESOME black glaze all by itself.
The are 8 clay bodies with .5 increase and decrease variations of CoTE. Basically cover a range of 4-7, the magic number is still 5.7.
The are 8 clay bodies with .5 increase and decrease variations of CoTE. Basically cover a range of 4-7, the magic number is still 5.7.
12 new clay bodies I'm testing with ice crackle glazes. 3 different firings. The top 7 tiles are new variations of my standard ice crackle with frit and bone ash additions and subtractions.
12 new clay bodies I’m testing with ice crackle glazes. 3 different firings. The top 7 tiles are new variations of my standard ice crackle with frit and bone ash additions and subtractions.
Studio table.
Studio table.
Three cups, same clay, same glaze, completely different firing and cooling regimes.
Three cups, same clay, same glaze, completely different firing and cooling regimes.

Jingdezhen Thrower – Large Vase

Taken in 2007 during my studies in Jingdezhen, China. This thrower uses the traditional gaolin china clay. I drew a picture of a large round vase with a small neck and then he proceeded to make exactly what I drew while also making the clay do some truly remarkable things!

Rutile, Ilmenite Variations of 1234 Base

1-10
1-10

Tenmoku Test Tiles – Iron, Rutile, Ilmenite, Earthenware Variants

In an efferot to further explore the different variations of Iron Oxide, Ilmenite, and Rutile – I’ve run a series of tests substituting Red Iron Oxide, for other oxides available in my lab. It was a pretty good series, although on some of the oxides, I overshot the ideal % and on a few I think it could be more.

Notice the 12% addition of Earthenware clays in 8,9, and 10 produce some pretty nice Celadon glazes!

MT Series
MT Series